3Cr2W8VΦ10 热作(压铸)模具钢 (轧材) 圆钢
3Cr2W8VΦ11 热作(压铸)模具钢 (轧材) 圆钢
3Cr2W8VΦ12 热作(压铸)模具钢 (轧材) 圆钢
3Cr2W8VΦ13 热作(压铸)模具钢 (轧材) 圆钢
3Cr2W8VΦ14 热作(压铸)模具钢 (轧材) 圆钢
3Cr2W8VΦ15 热作(压铸)模具钢 (轧材) 圆钢
3Cr2W8VΦ16 热作(压铸)模具钢 (轧材) 圆钢
3Cr2W8VΦ17 热作(压铸)模具钢 (轧材) 圆钢
3Cr2W8VΦ18 热作(压铸)模具钢 (轧材) 圆钢
3Cr2W8VΦ19 热作(压铸)模具钢 (轧材) 圆钢
3Cr2W8VΦ20 热作(压铸)模具钢 (轧材) 圆钢
3Cr2W8VΦ21 热作(压铸)模具钢 (轧材) 圆钢
3Cr2W8VΦ22 热作(压铸)模具钢 (轧材) 圆钢
3Cr2W8VΦ23 热作(压铸)模具钢 (轧材) 圆钢
3Cr2W8VΦ24 热作(压铸)模具钢 (轧材) 圆钢
3Cr2W8VΦ25 热作(压铸)模具钢 (轧材) 圆钢
3Cr2W8VΦ26 热作(压铸)模具钢 (轧材) 圆钢
3Cr2W8VΦ28 热作(压铸)模具钢 (轧材) 圆钢
3Cr2W8VΦ29 热作(压铸)模具钢 (轧材) 圆钢
3Cr2W8VΦ100 热作(压铸)模具钢 (锻材) 圆钢
3Cr2W8VΦ105 热作(压铸)模具钢 (锻材) 圆钢
3Cr2W8VΦ110 热作(压铸)模具钢 (锻材) 圆钢
3Cr2W8VΦ115 热作(压铸)模具钢 (锻材) 圆钢
3Cr2W8VΦ120 热作(压铸)模具钢 (锻材) 圆钢
3Cr2W8VΦ125 热作(压铸)模具钢 (锻材) 圆钢
3Cr2W8VΦ130 热作(压铸)模具钢 (锻材) 圆钢
3Cr2W8VΦ140 热作(压铸)模具钢 (锻材) 圆钢
3Cr2W8VΦ145 热作(压铸)模具钢 (锻材) 圆钢
3Cr2W8VΦ150 热作(压铸)模具钢 (锻材) 圆钢
3Cr2W8VΦ155 热作(压铸)模具钢 (锻材) 圆钢
3Cr2W8VΦ160 热作(压铸)模具钢 (锻材) 圆钢
3Cr2W8VΦ165 热作(压铸)模具钢 (锻材) 圆钢
3Cr2W8VΦ170 热作(压铸)模具钢 (锻材) 圆钢
3Cr2W8VΦ175 热作(压铸)模具钢 (锻材) 圆钢
---------------------
上海高高商贸有限公司：
阿里旺旺：shgaogaosu
联系人：粟太成
地址：上海市宝山区抚远路1288弄61号102室
----------------------------------
牌号：3Cr2W8V
材料名称：热作模具钢
执行标准GB/T。
特性与用途：3Cr2W8V热作模具钢，是常用的压铸模具钢，有较高的强度和硬度、耐冷热疲劳性良好，且有较好的淬透性，但其韧性和塑性较差。适用制作高温、高应力下，不受冲击负荷的凸模、凹模，如压铸模、热挤压模、精锻模、有色金属成型模等。
化学成分：
钴C0：30~0.40，
硅Si：0.40，
锰Mn：0.40，
铬Cr：2.20~2.70，
钨W：7.50~9.00，
钒V：0.20~0.50，
磷p：0.030，
硫S：0.030；
热处理及用途：
热处理：（交货状态：布氏硬度HBW10/3000（255~207）），淬火：1075~1125，冷却剂：油；
用途：常用的压铸模具钢。碳含量较低，有较高韧性和良好的导热性；同时，含有较多的碳化物形成元素铬、钨、钒，相变温度提高，使钢有高的高温强度、硬度和良好的耐热疲劳性；淬透。适于制造高温、高应力，但不受冲击负荷的压铸铜、铝、镁合金用附模、型芯、浇口套、分流钉、高应力压腊、热剪切刀、热顶锻模。
3Cr2W8V热作(压铸)模具钢上海高高特钢将以真信息、真品质、真价格的为您提供3Cr2W8V热作(压铸)模具钢材料！